A Comparative Study on the Temperature Effect of Solid Birch Wood and Solid Beech Wood under Impact Loading

Georg Baumann*, Reinhard Brandner, Ulrich Müller, Alexander Stadlmann, Florian Feist

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung

Abstract

In order to use wood for structural and load-bearing purposes in mechanical engineer-ing, basic information on the impact behaviour of the material over a wide temperature range is
needed. Diffuse porous hardwoods such as solid birch wood (Betula pendula) and solid beech wood (Fagus sylvatica) are particularly suited for the production of engineered wood products (EWPs) such
as laminated veneer lumber (LVL) or plywood due to their processability in a veneer peeling process.
In the frame of this study, solid birch wood and solid beech wood samples (300 × 20 × 20 mm3) were characterised by means of an impact pendulum test setup (working capacity of 150 J) at five
temperature levels, ranging from −30 ◦C to +90 ◦C. The pendulum hammer (mass = 15 kg) was equipped with an acceleration sensor in order to obtain the acceleration pulse and deceleration force
besides the impact bending energy. In both solid birch wood and solid beech wood, the deceleration forces were highest at temperatures at and below zero. While the average impact bending energy for solid birch wood remained almost constant over the whole considered temperature range, it was far less stable and prone to higher scattering for solid beech wood.
Originalspracheenglisch
Aufsatznummer7616
Seitenumfang17
FachzeitschriftMaterials
Jahrgang14
Ausgabenummer24
DOIs
PublikationsstatusVeröffentlicht - 1 Dez. 2021

ASJC Scopus subject areas

  • Physik der kondensierten Materie
  • Werkstoffwissenschaften (insg.)

Fingerprint

Untersuchen Sie die Forschungsthemen von „A Comparative Study on the Temperature Effect of Solid Birch Wood and Solid Beech Wood under Impact Loading“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren