Abstract
The aluminium alloy AA 6086 attains the highest room temperature strength among Al-Mg-Si alloys. This work studies the effect of Sc and Y on the formation of dispersoids in this alloy, especially L12-type ones, which can increase its high-temperature strength. A comprehensive investigation was carried out using light microscopy (LM), scanning (SEM), and transmission (TEM)
electron microscopy, energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and dilatometry to obtain the information regarding the mechanisms and kinetics of dispersoid formation, particularly during isothermal treatments. Sc and Y caused the formation of L12 dispersoids during heating to homogenization temperature and homogenization of the alloys, and during isothermal heat treatments of the as-cast alloys (T5 temper). The highest hardness of Sc and (Sc + Y) modified alloys was attained by heat-treating alloys in the as-cast state in the temperature range between 350 ºC and 450 ºC (via T5 temper).
electron microscopy, energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and dilatometry to obtain the information regarding the mechanisms and kinetics of dispersoid formation, particularly during isothermal treatments. Sc and Y caused the formation of L12 dispersoids during heating to homogenization temperature and homogenization of the alloys, and during isothermal heat treatments of the as-cast alloys (T5 temper). The highest hardness of Sc and (Sc + Y) modified alloys was attained by heat-treating alloys in the as-cast state in the temperature range between 350 ºC and 450 ºC (via T5 temper).
Originalsprache | englisch |
---|---|
Aufsatznummer | 2949 |
Seitenumfang | 24 |
Fachzeitschrift | Materials |
Jahrgang | 16 |
Ausgabenummer | 8 |
DOIs | |
Publikationsstatus | Veröffentlicht - 2023 |
ASJC Scopus subject areas
- Allgemeine Materialwissenschaften
- Physik der kondensierten Materie
- Werkstoffwissenschaften (insg.)
Fields of Expertise
- Advanced Materials Science
Treatment code (Nähere Zuordnung)
- Basic - Fundamental (Grundlagenforschung)