Hot deformation behavior of a ni‐based superalloy with suppressed precipitation

Franco Lizzi, Kashyap Pradeep, Aleksandar Stanojevic, Silvana Sommadossi, Maria Cecilia Poletti*

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung

Abstract

Inconel® 718 is a well‐known nickel‐based super‐alloy used for high‐temperature applications after thermomechanical processes followed by heat treatments. This work describes the evolution of the microstructure and the stresses during hot deformation of a prototype alloy named IN718WP produced by powder metallurgy with similar chemical composition to the matrix of In-conel® 718. Compression tests were performed by the thermomechanical simulator Gleeble® 3800 in a temperature range from 900 to 1025 °C, and strain rates scaled from 0.001 to 10 s−1. Flow curves of IN718WP showed similar features to those of Inconel® 718. The relative stress softening of the IN718WP was comparable to standard alloy Inconel® 718 for the highest strain rates. Large stress softening at low strain rates may be related to two phenomena: the fast recrystallization rate, and the coarsening of micropores driven by diffusion. Dynamic recrystallization grade and grain size were quantified using metallography. The recrystallization grade increased as the strain rate de-creased, although showed less dependency on the temperature. Dynamic recrystallization occurred after the formation of deformation bands at strain rates above 0.1 s−1 and after the formation of subgrains when deforming at low strain rates. Recrystallized grains had a large number of sigma 3 boundaries, and their percentage increased with strain rate and temperature. The calculated appar-ent activation energy and strain rate exponent value were similar to those found for Inconel® 718 when deforming above the solvus temperature.

Originalspracheenglisch
Aufsatznummer605
FachzeitschriftMetals
Jahrgang11
Ausgabenummer4
DOIs
PublikationsstatusVeröffentlicht - Apr. 2021

ASJC Scopus subject areas

  • Allgemeine Materialwissenschaften

Fingerprint

Untersuchen Sie die Forschungsthemen von „Hot deformation behavior of a ni‐based superalloy with suppressed precipitation“. Zusammen bilden sie einen einzigartigen Fingerprint.
  • CD-Labor für Design von Hochleistungslegierungen mittels thermo-mechanischer Prozesstechnik

    Poletti, M. C. (Teilnehmer (Co-Investigator)), Buzolin, R. H. (Teilnehmer (Co-Investigator)), Wang, R. (Teilnehmer (Co-Investigator)), Godavarthy Anantha Venkata, R. K. P. (Teilnehmer (Co-Investigator)), Miller Branco Ferraz, F. (Teilnehmer (Co-Investigator)), Fortmüller, S. (Teilnehmer (Co-Investigator)) & Baumann, G. (Teilnehmer (Co-Investigator))

    1/05/1730/04/25

    Projekt: Forschungsprojekt

Dieses zitieren