Influence of Plastic Deformation on the Hydrogen Embrittlement Susceptibility of Dual Phase Steels

Andreas Drexler*, Besim Helic, Zahra Silvayeh, Christof Sommitsch, Klemens Mraczek, Josef Domitner

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftKonferenzartikelBegutachtung

Abstract

The susceptibility of advanced high-strength steels (AHSS) to hydrogen embrittlement (HE) limits the broad utilization of these materials for body-in-white (BIW) components. The considerable decrease of both ductility and toughness due to local hydrogen accumulation inside of formed components may cause unpredictable time-delayed failure. In particular deep-drawn and punched AHSS components are prone to hydrogen absorption. This work investigates the influence of plastic deformation on hydrogen absorption of dual phase (DP) steels. For that purpose, tensile samples were machined out of three commercial 1.2 mm-thick DP sheets with ultimate tensile strengths of 626 MPa, 826 MPa and 1096 MPa. Samples were uniaxially pre-strained to 2 %, 5 %, 10 %, 15 % and 20 %. After pre-straining the samples were electrochemically charged with hydrogen, and the actual hydrogen contents were determined using a thermal desorption analyser (TDA). Before and after charging, the hardness of the samples was measured and the uniaxial quasi-static tensile properties were determined. In order to quantify the influence of plastic deformation on HE, slow strain rate tests (SSRT) were performed. The results of the tests were correlated with the fraction of martensite determined for each of the three steels.
Originalspracheenglisch
Seiten (von - bis)2077-2091
Seitenumfang15
FachzeitschriftKey Engineering Materials
Jahrgang926
DOIs
PublikationsstatusVeröffentlicht - 2022

Fields of Expertise

  • Mobility & Production

Fingerprint

Untersuchen Sie die Forschungsthemen von „Influence of Plastic Deformation on the Hydrogen Embrittlement Susceptibility of Dual Phase Steels“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren