NaNbO3-based antiferroelectric multilayer ceramic capacitors for energy storage applications

Lovro Fulanović*, Mao Hua Zhang, Yuping Fu, Jurij Koruza, Jürgen Rödel

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung


Antiferroelectric materials feature electric-field-induced phase transitions followed by a large polarization change characterized by double polarization hysteresis loops. Therefore, antiferroelectrics are engaging for high-energy density and high-power density applications, especially in the form of multilayer ceramic capacitors (MLCCs). However, the development of lead-free antiferroelectrics with stable double hysteresis loops is still challenging, especially for compositions based on NaNbO3. To this end, we have prepared MLCCs with the newly developed antiferroelectric composition 0.90NaNbO3-0.06SrSnO3-0.04(Na0.5Bi0.5)TiO3. The double hysteresis loops were determined at 24 kV/mm in the temperature range of 25–150 °C, with resulting recoverable energy storage ranging from 1.16 to 1.42 J/cm3, respectively. Moreover, the energy efficiency is rather constant at 0.4 in the same temperature range. Finally, the MLCCs exhibit resistance to electric field cycling and could withstand up to 1000 cycles. These results verify that NaNbO3-based antiferroelectrics in the form of MLCCs are promising for use in applications.

Seiten (von - bis)5519-5525
FachzeitschriftJournal of the European Ceramic Society
PublikationsstatusVeröffentlicht - Sept. 2021
Extern publiziertJa

ASJC Scopus subject areas

  • Keramische und Verbundwerkstoffe
  • Werkstoffchemie

Fields of Expertise

  • Advanced Materials Science


Untersuchen Sie die Forschungsthemen von „NaNbO3-based antiferroelectric multilayer ceramic capacitors for energy storage applications“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren