(Na1/2Bi1/2)TiO3-based lead-free co-fired multilayer actuators with large strain and high fatigue resistance

Haibo Zhang; Weigang Ma; Bing Xie; Ling Zhang; Shuxiang Dong; Pengyuan Fan; Ke Wang; Jurij Koruza; Jürgen Rödel

doi:10.1111/jace.16499

(Na_1/2Bi_1/2)TiO₃-based lead-free co-fired multilayer actuators with large strain and high fatigue resistance

Haibo Zhang^*, Weigang Ma, Bing Xie, Ling Zhang, Shuxiang Dong, Pengyuan Fan, Ke Wang, Jurij Koruza, Jürgen Rödel

^*Korrespondierende/r Autor/-in für diese Arbeit

Institut für Werkstoffkunde, Fügetechnik und Umformtechnik (3030)

Publikation: Beitrag in einer Fachzeitschrift › Artikel › Begutachtung

Abstract

Large-strain multilayer actuators (MLAs) were fabricated by tape-casting 0.91(Na_1/2 Bi_1/2)TiO₃–0.06BaTiO₃–0.03AgNbO₃(NBT-BT–3AN) lead-free incipient piezoceramics co-fired with Pt inner electrodes. Microstructures, dielectric properties, unipolar and bipolar strain, as well as fatigue properties of the MLAs were investigated. It was found that the actuator consisting of 15 ceramic layers with individual thicknesses of 114 μm could output a large unipolar strain of 0.3% and a dynamic displacement of 5 μm at 6 kV/mm at room temperature. It exhibited excellent cycling stability and provided a high strain of 0.23% after 10⁷ cycles at 6 kV/mm. Moreover, these MLAs still can deliver a strain of 0.20% at 125°C.

Originalsprache	englisch
Seiten (von - bis)	6147-6155
Seitenumfang	9
Fachzeitschrift	Journal of the American Ceramic Society
Jahrgang	102
Ausgabenummer	10
DOIs	https://doi.org/10.1111/jace.16499
Publikationsstatus	Veröffentlicht - 2019

ASJC Scopus subject areas

Keramische und Verbundwerkstoffe
Werkstoffchemie

Zugriff auf Dokument

10.1111/jace.16499

Andere Dateien und Links

Verknüpfung zur Publikation in Scopus

Dieses zitieren

@article{6c3890c07a5b499ab9bdab398551795d,

title = "(Na1/2Bi1/2)TiO3-based lead-free co-fired multilayer actuators with large strain and high fatigue resistance",

abstract = "Large-strain multilayer actuators (MLAs) were fabricated by tape-casting 0.91(Na1/2 Bi1/2)TiO3–0.06BaTiO3–0.03AgNbO3(NBT-BT–3AN) lead-free incipient piezoceramics co-fired with Pt inner electrodes. Microstructures, dielectric properties, unipolar and bipolar strain, as well as fatigue properties of the MLAs were investigated. It was found that the actuator consisting of 15 ceramic layers with individual thicknesses of 114 μm could output a large unipolar strain of 0.3% and a dynamic displacement of 5 μm at 6 kV/mm at room temperature. It exhibited excellent cycling stability and provided a high strain of 0.23% after 107 cycles at 6 kV/mm. Moreover, these MLAs still can deliver a strain of 0.20% at 125°C.",

keywords = "cycling stability, large strain, lead-free piezoceramics, multilayer actuators, temperature stability",

author = "Haibo Zhang and Weigang Ma and Bing Xie and Ling Zhang and Shuxiang Dong and Pengyuan Fan and Ke Wang and Jurij Koruza and J{\"u}rgen R{\"o}del",

note = "Funding Information: The authors acknowledge the generous support by the National Natural Science Foundation of China under grant no. 51672092, U1732117 and the China Postdoctoral Science Foundation under grant no. 2018M632847. H.Z. also thanks the Alexander-von-Humboldt foundation for generous funding and the generous support by Wuhan Morning Light Plan of Youth Science and Technology (No. 2017050304010299). Publisher Copyright: {\textcopyright} 2019 The American Ceramic Society",

year = "2019",

doi = "10.1111/jace.16499",

language = "English",

volume = "102",

pages = "6147--6155",

journal = "Journal of the American Ceramic Society",

issn = "0002-7820",

publisher = "Wiley-Blackwell",

number = "10",

}

TY - JOUR

T1 - (Na1/2Bi1/2)TiO3-based lead-free co-fired multilayer actuators with large strain and high fatigue resistance

AU - Zhang, Haibo

AU - Ma, Weigang

AU - Xie, Bing

AU - Zhang, Ling

AU - Dong, Shuxiang

AU - Fan, Pengyuan

AU - Wang, Ke

AU - Koruza, Jurij

AU - Rödel, Jürgen

N1 - Funding Information: The authors acknowledge the generous support by the National Natural Science Foundation of China under grant no. 51672092, U1732117 and the China Postdoctoral Science Foundation under grant no. 2018M632847. H.Z. also thanks the Alexander-von-Humboldt foundation for generous funding and the generous support by Wuhan Morning Light Plan of Youth Science and Technology (No. 2017050304010299). Publisher Copyright: © 2019 The American Ceramic Society

PY - 2019

Y1 - 2019

N2 - Large-strain multilayer actuators (MLAs) were fabricated by tape-casting 0.91(Na1/2 Bi1/2)TiO3–0.06BaTiO3–0.03AgNbO3(NBT-BT–3AN) lead-free incipient piezoceramics co-fired with Pt inner electrodes. Microstructures, dielectric properties, unipolar and bipolar strain, as well as fatigue properties of the MLAs were investigated. It was found that the actuator consisting of 15 ceramic layers with individual thicknesses of 114 μm could output a large unipolar strain of 0.3% and a dynamic displacement of 5 μm at 6 kV/mm at room temperature. It exhibited excellent cycling stability and provided a high strain of 0.23% after 107 cycles at 6 kV/mm. Moreover, these MLAs still can deliver a strain of 0.20% at 125°C.

AB - Large-strain multilayer actuators (MLAs) were fabricated by tape-casting 0.91(Na1/2 Bi1/2)TiO3–0.06BaTiO3–0.03AgNbO3(NBT-BT–3AN) lead-free incipient piezoceramics co-fired with Pt inner electrodes. Microstructures, dielectric properties, unipolar and bipolar strain, as well as fatigue properties of the MLAs were investigated. It was found that the actuator consisting of 15 ceramic layers with individual thicknesses of 114 μm could output a large unipolar strain of 0.3% and a dynamic displacement of 5 μm at 6 kV/mm at room temperature. It exhibited excellent cycling stability and provided a high strain of 0.23% after 107 cycles at 6 kV/mm. Moreover, these MLAs still can deliver a strain of 0.20% at 125°C.

KW - cycling stability

KW - large strain

KW - lead-free piezoceramics

KW - multilayer actuators

KW - temperature stability

UR - http://www.scopus.com/inward/record.url?scp=85065422715&partnerID=8YFLogxK

U2 - 10.1111/jace.16499

DO - 10.1111/jace.16499

M3 - Article

AN - SCOPUS:85065422715

SN - 0002-7820

VL - 102

SP - 6147

EP - 6155

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

IS - 10

ER -