Parallelized biocatalytic scanning probe lithography for the additive fabrication of conjugated polymer structures

Joseph Hosford, Morgane Valles, Florian W. Krainer, Anton Glieder, Lu Shin Wong*

*Korrespondierende/r Autor/-in für diese Arbeit

Publikation: Beitrag in einer FachzeitschriftArtikelBegutachtung

Abstract

Scanning probe lithography (SPL) offers a more accessible alternative to conventional photolithography as a route to surface nanofabrication. In principle, the synthetic scope of SPL could be greatly enhanced by combining the precision of scanning probe systems with the chemoselectivity offered by biocatalysis. This report describes the development of multiplexed SPL employing probes functionalized with horseradish peroxidase, and its subsequent use for the constructive fabrication of polyaniline features on both silicon oxide and gold substrates. This polymer is of particular interest due to its potential applications in organic electronics, but its use is hindered by its poor processability, which could be circumvented by the direct in situ synthesis at the desired locations. Using parallelized arrays of probes, the lithography of polymer features over 1 cm2 areas was achieved with individual feature widths as small as 162 ± 24 nm. The nature of the deposited materials was confirmed by Raman spectroscopy, and it was further shown that the features could be chemically derivatized postlithographically by Huisgen [2 + 3] "click" chemistry, when 2-propargyloxyaniline was used as the monomer in the initial lithography step.

Originalspracheenglisch
Seiten (von - bis)7185-7193
Seitenumfang9
FachzeitschriftNanoscale
Jahrgang10
Ausgabenummer15
DOIs
PublikationsstatusVeröffentlicht - 2018

ASJC Scopus subject areas

  • Werkstoffwissenschaften (insg.)

Fields of Expertise

  • Human- & Biotechnology

Fingerprint

Untersuchen Sie die Forschungsthemen von „Parallelized biocatalytic scanning probe lithography for the additive fabrication of conjugated polymer structures“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren