Homogeneous cellulose thin films by regeneration of cellulose xanthate: properties and characterization

Michael Weißl, Katrin Niegelhell, David Reishofer, Armin Zankel, Josef Innerlohinger, Stefan Spirk

Research output: Contribution to journalArticlepeer-review


The preparation and characterization of cellulose thin films derived from cellulose xanthate is reported. The films are prepared by depositing alkaline aqueous solutions of cellulose xanthate onto silicon wafers, followed by a spin coating step. Depending on the xanthate concentration used for spin coating, films with 50 and 700 nm thickness are obtained. The cellulose xanthate is converted to cellulose by exposing the films to HCl vapors over a period of 20 min. The conversion is monitored by ATR-IR spectroscopy, which allows for tracking the rupture of C–S and C=S bonds during the regeneration process. The conversion is accompanied by a reduction of the film thickness of ca 40% due to the removal of the bulky xanthate group. The films feature a homogenous, but porous morphology as shown by atomic force microscopy. Further, the films were investigated towards their interaction with Bovine Serum Albumin (BSA) and fibrinogen by means of multi-parameter surface plasmon resonance spectroscopy. Similar as other cellulose thin films BSA adsorption is low while fibrinogen adsorbs to some extent at physiological pH (7.4).
Original languageEnglish
Pages (from-to)711-721
Number of pages11
Issue number1
Publication statusPublished - 2018

Fields of Expertise

  • Advanced Materials Science

Cite this