Thermomechanical degradation of polyetherimide (PEI) by friction-based joining and the effects on quasi-static mechanical strength of hybrid joints

M. Sônego, A.B. Abibe, S.V. Canevarolo Jr., S.H.P. Bettini, J.F. dos Santos, L.B. Canto, S. T. Amancio-Filho

Research output: Contribution to journalArticlepeer-review

Abstract

This study investigated quantitatively the thermomechanical degradation of polyetherimide (PEI) due to Friction-based Injection Clinching Joining (F-ICJ) and the effects on the mechanical strength of hybrid joints with aluminum. PEI samples extracted from process-affected regions of the joints were characterized in terms of their molecular weight distribution (MWD) and glass transition temperature (Tg), while mechanical strength of the joints was evaluated by cross tensile testing. PEI samples produced by the most severe joining condition showed decrease of 37 % of number-average molecular weight (Mn) and 17 % of weight-average molecular weight (Mw), while polydispersity index (Mw/Mn) increased 33 % as compared with as-received polymer. The chain scission distribution function (CSDF) indicated non-random multiple scissions as the main degradation mechanism of PEI due to F-ICJ. From the dependence of Tg with Mn the parameters of the Fox-Flory equation for PEI were obtained. A fractional factorial design of experiments was adopted to analyze the influence of the process parameters on the polymer degradation, based on Tg values. High level of PEI degradation and microstructural defects caused by high energy inputs have combined negative effect on the ultimate cross tensile force and displacement of joints. In general, these results can contribute to the knowledge of thermomechanical degradation of PEI and help with the optimization of F-ICJ.
Original languageEnglish
Pages (from-to)100-110
JournalInternational Polymer Processing
Volume34
Issue number1
DOIs
Publication statusPublished - 2019

Fingerprint

Dive into the research topics of 'Thermomechanical degradation of polyetherimide (PEI) by friction-based joining and the effects on quasi-static mechanical strength of hybrid joints'. Together they form a unique fingerprint.

Cite this