UV-Induced reduction of graphene oxide in cellulose nanofibril composites

Y. B. Pottathara, Sabu Thomas, N. Kalarikkal, Thomas Grießer, Y. Grohens, V. Bobnar, M. Finšgar, V. Kokol, R. Kargl

Research output: Contribution to journalArticlepeer-review


We report on an effective dry method to reduce graphene oxide (GO) in films of cellulose nanofibrils (CNF) by UV irradiation in the presence of nitrogen gas. The reduction of GO and the removal of carbonyl and carboxyl moieties were confirmed by infrared and UV-vis spectroscopy, potentiometric charge titration and X-ray photoelectron spectroscopy (XPS). The crystallinity of native and reduced composites was elucidated by X-ray diffraction measurements. The resulting reduced graphene oxide-CNF nanocomposite films remain flexible and show improved dielectric properties. After 5 hours of UV irradiation a 3 wt% graphene oxide loaded film increased its dielectric constant from 68.9 to 88.9, which shows significant enhancement compared to previous reports. The AC conductivity of reduced GO films reaches values of 9.37 × 10 −4 S m −1 . The electrochemical performance of the samples was tested by cyclic voltammetry and electrochemical impedance spectroscopy. UV treated samples showed a higher capacitive nature than untreated samples. The UV induced reduction of GO in the presence of CNF is seen as a promising alternative to solvent based methods.

Original languageEnglish
Pages (from-to)681-688
Number of pages8
JournalNew Journal of Chemistry
Issue number2
Publication statusPublished - 1 Jan 2019

ASJC Scopus subject areas

  • Catalysis
  • Chemistry(all)
  • Materials Chemistry

Fields of Expertise

  • Advanced Materials Science


Dive into the research topics of 'UV-Induced reduction of graphene oxide in cellulose nanofibril composites'. Together they form a unique fingerprint.

Cite this