Abstract
The heat-treatment (HT) schedule and selected annealing parameters have a substantial effect on the microstructure and mechanical properties of medium-Mn-steels. The structure morphology depends on the fact, whether the austenite-reverted transformation takes place from deformed (one-step HT) or non-deformed (two-step HT) microstructures. Depending on the intercritical annealing temperature, the stability of the retained austenite can be altered to a large extent. As a result, the mechanical properties can be adjusted from high strength with excellent ductility to very high strength with reasonable ductility. The present contribution, therefore, elucidates the dependence of the microstructural characteristics and material behaviour on the HT parameters for medium-Mn alloy compositions with different Mn-contents.
Originalsprache | englisch |
---|---|
Fachzeitschrift | Materials Science and Technology |
Frühes Online-Datum | 30 Nov. 2018 |
DOIs | |
Publikationsstatus | Elektronische Veröffentlichung vor Drucklegung. - 30 Nov. 2018 |
ASJC Scopus subject areas
- Allgemeine Materialwissenschaften
- Physik der kondensierten Materie
- Werkstoffmechanik
- Maschinenbau