In situ small-angle X-ray scattering (SAXS) was employed to identify critical parameters during thermal treatment for template removal of an ordered mesoporous carbon precursor synthesized via a direct soft-templating route. The structural parameters obtained from the SAXS data as a function of time were the lattice parameter of the 2D hexagonal structure, the diameter of the cylindrical mesostructures and a power-law exponent characterizing the interface roughness. Moreover, detailed information on contrast changes and pore lattice order was obtained from analysis of the integrated SAXS intensity of the Bragg and diffuse scattering separately. Five characteristic regions during heat treatment were identified and discussed regarding the underlying dominant processes. The influence of temperature and O2/N2 ratio on the final structure was analyzed, and parameter ranges were identified for an optimized template removal without strongly affecting the matrix.
Originalsprache | englisch |
---|---|
Seiten (von - bis) | 801-809 |
Seitenumfang | 9 |
Fachzeitschrift | Journal of Applied Crystallography |
Jahrgang | 56 |
Ausgabenummer | 3 |
DOIs | |
Publikationsstatus | Veröffentlicht - 1 Juni 2023 |
ASJC Scopus subject areas
- Allgemeine Biochemie, Genetik und Molekularbiologie
Fields of Expertise
- Advanced Materials Science
Fingerprint
Untersuchen Sie die Forschungsthemen von „Optimizing surfactant removal from a soft-templated ordered mesoporous carbon precursor: an in situ SAXS study“. Zusammen bilden sie einen einzigartigen Fingerprint.Projekte
- 1 Laufend
-
Strukturcharakterisierung mittels Licht- und Röntgenstreuung
Marmiroli, B., Sartori, B. & Amenitsch, H.
31/07/15 → 31/12/30
Projekt: Arbeitsgebiet