TY - JOUR
T1 - Bioactive albumin functionalized polylactic acid membranes for improved biocompatibilty
AU - Nyanhongo, Gibson Stephen
AU - Diaz Rodriguez, Rosario
AU - Nugroho Prasetyo, Endry
AU - Cristina, Caparrós
AU - Ribeiro, C.
AU - Sencadas, V.
AU - Lanceros-Mendez, S.
AU - Herrero Acero, Enrique
AU - Gübitz, Georg
PY - 2013
Y1 - 2013
N2 - Biocompatibility is a major challenge for successful application of many biomaterials. In this study the ability to coat chemically and enzymatically activated poly(L-lactic acid) (PLA) membranes with heat denatured human serum albumin to improve biocompatibility was investigated. PLA membranes hydrolyzed with NaOH or cutinase and then treated with 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, hydrochloride (EDAC) as a heterobifunctional cross-linker promoted the coupling single bondCOOH groups on PLA membranes and single bondNH2 groups of heat denatured human serum albumin. This resulted in increased hydrophilicity (lowest water contact angles of 43° and 35°) and highest antioxidant activity (quenching of 79 μM and 115 μM tetramethylazobisquinone (TMAMQ) for NaOH and cutinase pretreated membranes, respectively). FTIR analysis of modified PLA membranes showed new peaks attributed to human serum albumin (amide bond, NH2 and side chain stretching) appearing within 3600–3000 cm−1 and 1700–1500 cm−1 (Fig. 3). MTT studies also showed that osteoblasts-like and MC-3T3-E1 cells viability increased 2.4 times as compared to untreated PLA membranes. The study therefore shows that this strategy of modifying the surfaces of PLA polymers could significantly improve biocompatibility.
AB - Biocompatibility is a major challenge for successful application of many biomaterials. In this study the ability to coat chemically and enzymatically activated poly(L-lactic acid) (PLA) membranes with heat denatured human serum albumin to improve biocompatibility was investigated. PLA membranes hydrolyzed with NaOH or cutinase and then treated with 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide, hydrochloride (EDAC) as a heterobifunctional cross-linker promoted the coupling single bondCOOH groups on PLA membranes and single bondNH2 groups of heat denatured human serum albumin. This resulted in increased hydrophilicity (lowest water contact angles of 43° and 35°) and highest antioxidant activity (quenching of 79 μM and 115 μM tetramethylazobisquinone (TMAMQ) for NaOH and cutinase pretreated membranes, respectively). FTIR analysis of modified PLA membranes showed new peaks attributed to human serum albumin (amide bond, NH2 and side chain stretching) appearing within 3600–3000 cm−1 and 1700–1500 cm−1 (Fig. 3). MTT studies also showed that osteoblasts-like and MC-3T3-E1 cells viability increased 2.4 times as compared to untreated PLA membranes. The study therefore shows that this strategy of modifying the surfaces of PLA polymers could significantly improve biocompatibility.
U2 - 10.1016/j.reactfunctpolym.2012.12.007
DO - 10.1016/j.reactfunctpolym.2012.12.007
M3 - Article
SN - 1873-166X
VL - 73
SP - 1399
EP - 1404
JO - Reactive & Functional Polymers
JF - Reactive & Functional Polymers
IS - 10
ER -